RectorSeal NOKORODE Pre-Tinning Paste Flux, Series: 95/5, 8 oz, Jar, 0 g/L VOC, Paste, Composition: 10 to 25% Zinc Chloride, 10 to 25% Ammonium Chloride, <10% Zinc Oxide, Tin, <1% Antimony, Tan/Gold to Black, Petroleum, >399 degree Fahrenheit Flash, 120 to 150 degree Fahrenheit Melting, Flammability: 1, 1.59 Specific Gravity, Applicable Materials: Copper/Tin/Zinc/Nickel/Sheet Lead
Nokorode pre-tinning paste flux is a creamy-smooth paste specifically formulated with a small amount of 95/5 tin/antimony solder powder inch the formula and a heat indicator. It is formulated to clean, pretin and flux the joint all at one time. Provides a fast, safe method of fluxing most common metals and solders. Excellent for use on larger diametermeters fittings or faster soldering's of smaller diametermeter fittings because it automatically tins before reaching higher temperature.
Features
Features
Produces excellent, leak-free soldered joints
Smooth stable paste for easy brush on application
Contains small amount of 95/5 solder powder
2 years minimum shelf life
Wt/gal at 77 deg F: 8.44 +/- 0.5 lb/gal
Do not use on magnesium or aluminum
Recommended for 95/5 or 50/50 solder applications
Lead-free - formula is safe for use on potable systems
Cleans, pre-tins and fluxes
Great for large diameter fittings or faster soldering of small diameter fittings because it automatically tins before a high temperature is reached
Cuts waste
Very low scorching or burning
Very low corrosive properties prevents pitting
Very low spattering
Excellent wetting ability allows solder to flow easily and uniformly into joints
Applicable Materials: Copper/Tin/Zinc/Nickel/Sheet Lead
Form: Paste
Melting Range: 120 to 150 deg F
Odor/Scent: Petroleum
Specific Gravity: 1.59
VOC Content: 0 g/L
Warranty: Limited
Capacity: 8 oz
Color: Tan/Gold to Black
Composition: 10 to 25% Zinc Chloride, 10 to 25% Ammonium Chloride, <10% Zinc Oxide, Tin, <1% Antimony